Effect of silver nanoparticle on properties of maxillofacial silicone elastomer material
Aim: The purpose of this study was to evaluate the impact of silver nanoparticle incorporation into maxillofacial silicone material on its hardness tear strength and color stability. Methodology: A total of 90 silicone specimens were fabricated. The control samples were fabricated with- out silver nanoparticles and test samples were fabricated with 20 ppm concentration of silver nanoparticles. Digital shore A hardness tests was used to measure ha…
Comparative evaluation of fracture resistance of hyflex edm, neolix neo niti, protaper next and protaper gold files- an in-vitro study
Aim: The purpose of the present research was to assess the comparison of the fracture resistance ability of various endodontic files like- Hyflex EDM, Neolix Neo NiTi, Protaper Next and Protaper Gold. Methodology: All the instruments were subjected to fracture test using a stainless-steel artificial canal. Time required for fracture as well as number of cycles to failure was calculated at 5 and 8 mm distance from the end of root canal tip. The fr…
No prominent works on this page.
Effect of silver nanoparticle on properties of maxillofacial silicone elastomer material
Aim: The purpose of this study was to evaluate the impact of silver nanoparticle incorporation into maxillofacial silicone material on its hardness tear strength and color stability. Methodology: A total of 90 silicone specimens were fabricated. The control samples were fabricated with- out silver nanoparticles and test samples were fabricated with 20 ppm concentration of silver nanoparticles. Digital shore A hardness tests was used to measure ha…
Comparative evaluation of fracture resistance of hyflex edm, neolix neo niti, protaper next and protaper gold files- an in-vitro study
Aim: The purpose of the present research was to assess the comparison of the fracture resistance ability of various endodontic files like- Hyflex EDM, Neolix Neo NiTi, Protaper Next and Protaper Gold. Methodology: All the instruments were subjected to fracture test using a stainless-steel artificial canal. Time required for fracture as well as number of cycles to failure was calculated at 5 and 8 mm distance from the end of root canal tip. The fr…
Composite material (2 works) · Materials Science (2 works) · Mathematics (2 works) · Significant difference (2 works) · Chemistry (1 work) · Control sample (1 work) · Corneal Surgery and Treatments (1 work) · Cyclic stress (1 work) · Dental Radiography and Imaging (1 work) · Dental Research and COVID-19 (1 work)